TechXT-AR Large-Format Acrylic Sheets with Anti-Reflective (AR) Coating
For applications requiring large pieces of anti-reflective acrylic coatings, we stock large-format extruded acrylic sheets with hard-coat and anti-reflective coats on both sides.
These sheets start with commercial grade clear extruded acrylic, followed by flow coated hard-coat on both sides, and are finished with a vacuum deposition multi-layer anti-reflective coating on both sides. An additional oleophobic coating is added to both sides to make it easier to keep the material clean. The result is a clear acrylic sheet with very low reflections (<2%) and high transmission (>98%) across the visible range. We stock the sheets in large sizes, typically 48 x 96″, so these are well suited for larger display applications.
Note: This is not CLAREX brand material
Benefits
- High Transmission (>98%) and Low Reflection (<2%) in the visible range
- Large-Format – Typically up to 48×96″, but larger sizes could be arranged
- Good scratch and chemical resistance
- UV Stable
- Excellent machinability and laser-cutting performance
- Lightweight
- Oleophobic surfaces help to keep it clean
- Could be made custom with AR coating on 1 side only

Applications
- Information Displays
- Kiosks
- Outdoor Readable Displays
- Lighting
Thicknesses
- 2.0mm (0.079″)
- 3.0mm (0.118″)
- 4.5mm (0.177″)
- 6.0mm (0.237″)
Size
- 48 x 96″ standard
- Larger sizes possible

Physical Properties of TechXT Anti-Reflective Coated Extruded Acrylic
Property | Method | Unit | Value |
---|---|---|---|
Total Visible Transmission | % | >97 | |
Total Visible Reflection | % | <1.50 | |
Specific Gravity | ASTM D-792 | 1.19 | |
Tensile Strength | ASTM D-638 | psi | 11,000 |
Modulus of Elasticity | ASTM D-638 | psi | 490,000 |
Flexural Strength | ASTM D-790 | psi | 17,000 |
Maximum Recommended Continuous Temperature | °F | 185 | |
Coefficient of Thermal Expansion | ASTM D-696 | in/in/ºF | 3.0 x 10-5 |
Deflection Temperature | ASTM D-648 | °F | 203 |
Cold Resistance | -40ºC x 100hr | No Change | |
Abrasion Resistance | Dry Cloth Rub Test, 2.5lb load Alcohol Soaked Cloth Rub Test, 2.5lb load | 600 Strokes 20 Strokes | |
Weatherability | High Humidity: 50ºC, 95% RH Salt Fog: 40days, 5%NaCl, 35ºC | No Change | |
UV Stability | 2000hr Arc Test at 100,000 LUX | No Change | |
Coating Adhesion | Snap Tape Test | No change | |
Pencil Hardness | >5H | ||
Flammability Rating | UL 94HB | ||
Contact Angle | 100º | ||
CHEMICAL RESISTANCE (24hr immersion) | |||
Isopropyl Alcohol (50%) | No Change | ||
Windex Cleaner, with and without ammonia | No Change | ||
Distilled Water | No Change | ||
Artificial Perspiration (5mg NaCl, 5ml Acetic Acid, 3ml Butyric Acid, 84ml Distilled Water) | No Change | ||
Acetone | No Change | ||
Coffee | No Change | ||
Coke | No Change | ||
Saline Solution (170g NaCl per 3.8l of water) | No Change |